JIS G3463 SUS304TB, SUS316TB, SUS347HTB Boiler Tube

JIS G3463 SUS304TB, SUS316TB, SUS347HTB Boiler Tube
GRADE: SUS304TB stainless steel pipe, SUS316TB stainless steel tube, SUS347HTB...
STANDARD: JIS G3463
CHEMICAL REQUIREMENTS:
:% Max
GRADE
C
Mn
S
P
Si
Ni
Cr
SUS304TB
0.08
2.00
0.03
0.04
1.00
8.0-11.0
18.0-20.0
MECHANICAL PROPERTY:
Material
Tensile Strength
,min MPa
Yield Strength(0.2% offset),
min MPa
Elongation in 2 in. Or 50mm(or 4 D) min,%
SUS304TB
520
205
OD＜10mm, 27
10mm＜OD＜20mm, 30
20mm＜OD, 35
APPLICATION of Ferritic Stainless Steel Pipe:
Used as Boiler and Heat Exchanger Tubes.

评论

发表评论

此博客中的热门博文

WELCOME TO BAOSTEEL

图片
Baosteel Special Metals Co., Ltd., formerly known as Shanghai No. 5 Steel Plant, was founded in September 1958 and was awarded the honorary title of State-level Enterprise and National Quality Management Award. It is known as the leader of China's special steel industry. In November 1998, Shanggang No. 5 Plant was integrated into Baosteel Group and changed its name to Baosteel Group Shanghai Wugang Co., Ltd. In May 2005, the company's core assets were acquired by Baoshan Iron & Steel Co., Ltd., and the group was established as a special steel branch of Baosteel Co., Ltd. In June 2018, in accordance with the new round of strategic planning of "One Base and Five Yuans", China Baowu Group further promoted the development of "one place and two industries" of special steel land, and established Baowu Special Metallurgical Co., Ltd. (referred to as Baowu Special Metallurgy Co., Ltd.) ), Baowu Special Metallurgy will strive to become "the leader of th...
阅读全文

Why chose Stainless Steel Pipe Ferritic?

图片
　 Stainless Steel Pipe Ferritic  is generally nickel-free. The main alloying element is chromium. This steel contains relatively low carbon and often contains ferrite forming elements such as aluminum to ensure that the steel is mainly ferrite. The chromium content is generally between 12% and 30%, and the carbon content is mostly less than 0.12%. Ferritic stainless steel is roughly divided into Cr11%-15%, Cr16%-20% and Cr21-30% according to the chromium content in the steel. In addition to stainless steel and local corrosion resistance, ferritic stainless steel is resistant to chloride. Stress corrosion, pitting corrosion resistance, crevice corrosion resistance and other local corrosion performance are the main features of corrosion resistance of such steel. Ferritic stainless steel has high strength and low cold work hardening tendency. Its thermal conductivity is 130%-150% of austenitic stainless steel, and the coefficient of linear expansion is 60% to 70% of austenitic stainl...
阅读全文

Three Major Causes of Oxidation in Stainless Steel

图片
As a  Nickel Alloy Pipe Factory , let's talk about the reasons why stainless steel often oxidizes. 1. Production process reasons: This is one of the causes of oxidation of steel products. From the perspective of the production process and product characteristics, forming a thin oxide film on the surface of the product is the basic process to avoid oxidation and steel products. One of the main features that distinguish it from other steel products. However, when the production process is insufficient or inadvertent, the oxide film in the air is incomplete and discontinuous, and the oxygen in the air directly undergoes a redox reaction with some elements in the product, thereby causing the product to exhibit oxidation. 2. Reasons for the proportion of products: Some manufacturers reduce the proportion of important elements such as chromium and nickel to reduce the production cost, and increase the content of other factors such as carbon. This production phenomenon, which is not ...
阅读全文